      The key factors in determining the quality of a brazed joint are the method of brazing,

the composition of the brazing filler metal and the flux. For use as a filler material, a

metal or alloy must have a lower melting point than the workpiece material, and must be

able to wet the workpiece material. In addition, when molten, it must flow sufficiently

easily to enable it properly to fill the joint. The resulting alloy must provide the neces-

sary mechanical and physical properties, while the filler metal must not be vaporised to

any significant extent during the heating process, as this could result in poor fusion.

Metals in the following groups are those most commonly used as brazing filler metals:

see also Table 13.2.