       A major problem when welding austenitic steels was previously the need to avoid

carbide precipitations at the grain boundaries. These carbides are chromium-rich, and

therefore reduce the chromium concentration in the austenite adjacent to the grain

               boundaries, thus creating the conditions for intercrystalline corrosion 