Welded structures subjected to fatigue loads-2

Welded structures subjected to fatigue loads-2

The static strength of the parent metal (and of the filler metal) is of less importance in

determining the fatigue strength of a weldedjoint.

This phenomenon can be explained by the theory of fracture mechanics. We nor-

mally distinguish between three different phases in the growth of a fatigue crack through

the material:

Phase 1:Crack initiation = the number of load cycles required before the discontinui-

ties form a real crack (of the order of hundredths of a millimetre in size).

Phase 2:Crackpropagation = after formation, the crack grows by a given particular

length for each new load cycle.

                  Phase 3:Final failure = when the crack has grown so much