 demonstrates the microhardness values of the three welding areas

Supplied  By   RIHUI Ceramic Welding Backing

 

 

Table 3 demonstrates the microhardness values of the three welding areas of test sample C12 in accordance with
Figure 2.The base metal presented hardness values between 140 and 153 kgf/mm 2,TAZ presented values between 134
and 168 kgf/mm 2 and the weld metal values between 134 and147 kgf/mm2 .

These values indicate that no phases were formed both in the root pass and in the TAZ. In relation to Phase 2 of the paper,the aim was to
assess a joint welded using the one-sided welding technique.Figure 9 presents the appearance of the weld
bead with(a)the upper part and(b)the weld bead.Visual inspection and penetrant liquid did not detect any surface
discontinuities,and no adhesion of the ceramic material on the weld bead was observed.The macrograph of the cross section of the welded
joint in A36 steel plate with a thickness of 15.8 mm using acordierite ceramic backing is shown in Figure 10.It is possible to note areas 1–6 which demonstrate each of the