Martensitic steels--1

Martensitic steels--1

If the workpiece is welded in the hot state and then heat-treated, there is a risk of

hardening cracks in the transformation zone. There is also a risk of brittle cracking, as

the material has a relatively high brittle transition temperature, and welding-induced

stresses in and around the weld zone are significant. In addition, there is a risk of

hydrogen embrittlement in the HAZ, particularly if damp electrodes have been used.

Further, if using a filler material of the same metal as the base material, there is a risk of

transverse cracks in the weld metal, and so austenitic fillers are often used to reduce this

risk. This also reduces the risk of brittle failure.

. 