Results and discussion

Results and discussion

Phase 1 of this paper aimed to assess the appropriate welding parameters,the quality of the root pass and

efficiency of the cordierite ceramic backing produced welding process.In the other test samples,no disconti-

nuities were observed.One notes in the upper part of the weld of test sample C10,Figure 8(c),that the filling of the

welded joint was insufficient,in other words,the entire thickness of the plate.In fact,the aim of this phase is to

assess the first weld bead(root pass)produced using the ceramic backing.In the case of a welded joint,there is the

need to apply additional weld beads over this root pass, with the aim of filling the joint.The results obtained herein

are compliant with Andrade who presented the technical feasibility of welding the root pass with a ceramic backing

and the robotized fluxed core wire welding process, specifying the welding parameters of the 205 A current,

26 V voltage and welding speed of 20 cm/min,using a root face opening of 3 mm,a chamfer angle of 408 and 608 